How to choose material for silicone bracelet?

When producing silicone customized bracelet/wristband, many silicone product has Defects in performance and appearance , which is also called defective products. The products are closely related to what kinds of material you choose? So how should we choose the suitable material for the best silicone product? That’s the topic we gonna talk about today.

The difference of the density and hardness of material will lead to the different silicone product performance. For example, The density of the silicone material we used for the normal silicone product is 40-60 degree. For the silicone bracelet, the hardness is nearly 40-60 degree. the stretch can reach 150% with the 40 degree ,while it’s only 80% with the 60 degree hardness. So you need to choose what kinds of solid silicone material you need to use for the different product. Or you can also show the product you want to make to the professional silicone material supplier, they will give you any advice for this.

It would be harder to produce with the high hardness silicone material than the low degree material. For the manufacturer, The higher hardness degree you choose, the higher defective rate you’ll have. And it will also have bad influence with the degree stretch performance of product. It make the product easy to break. So , is it true that the lower hardness degree material will make better silicone bracelet?

Not, it doesn’t.

So what will happen with the lower silicone hardness material to make bracelet?

Silicone rubber products with lower hardness are most afraid of the softness of the product. Insufficient tension will cause the product's resilience and failure of the product's molecular chain. Therefore, to ensure normal use performance, low-hardness silicone bracelets are recommended not to be stretched for a long time. Low-hardness silicone The product needs to be vulcanized before it can be ejected normally. For example, in order to improve efficiency and reduce time during the production and processing of silicone manufacturers, it may cause the product to become soft and weak, and it will not rebound when it is stretched. If it is not a phenomenon caused during the production process, then it is necessary to find the reason from the raw materials